Stainless Steel 316L Flanges
Stainless Steel 316L Flanges Specification
| Size Chart | 1/2" to 48" |
|---|---|
| Pressure Rating ANSI | 2500#, 600#, 900#, 150#, 300#, 1500# |
| Most common types | Threaded / Forged / Screwed / Plate |
| Coating | Zinc Plated, Anti-rust Paint, Cold and Hot Dip Galvanized, Oil Black Paint, Yellow Transparent |
| Test Certificates | EN 10204/3.1B Raw Materials Certificate 100% Radiography Test Report Third Party Inspection Report, etc |
| Connect Type/ Flange Face Type | Flat Face, Ring Type Joint, Large Male-Female, Small Male-Female, Raised Face, Lap-Joint Face, Small Tongue, Large Tongue & Groove, Groove |
| Production technique |
|
| Equipment | Pushing Machine, Bending machine, electric bevelling machine, Press machine, Sand-blasting machine etc |
Chemical Composition of 316L Stainless Steel Blind Flange
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
|---|---|---|---|---|---|---|---|---|---|---|
| 316L | min. | – | – | – | – | – | 16.0 | 2.0-3.0 | 10.0 | – |
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | – | ||
Mechanical Properties of SS 316L Slip on Flange
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
|---|---|---|---|---|---|
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316L | 485 | 170 | 40 | 95 | 217 |
ASTM A182 F316L Reducing Flanges Physical Properties
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
|---|---|---|---|---|---|---|---|---|---|
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
316L SS Weld Neck Flange Equivalent Grade
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
|---|---|---|---|---|---|---|---|
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |